100%Biodegradable Polylactic Acid PLA pellets PLA granules PLA plastic raw material
وصف
100%Biodegradable Polylactic Acid PLA pellets PLA granules PLA plastic raw material
Extrusion Molding
PLA 102 is composed of PLA and PBAT, developed for the extrusion molding applications. See الطاولة 1 إلى عن على properties.
الطاولة 1- Typical Material Properties
Physical Properties | Result | Test Method |
كثافة (ز / سم 3) | 1.532 | ISO 1183-1:2012 طريقة أ |
Melt Mass Flow Rate (g/10min) | 1.62 | ISO 1133-1:2011 Procedure A |
Mechanical Properties |
| |
Flexural Strength (MPa) | 58.9 | ISO 178:2010/Amd. 1:2013 Method A |
Flexural Modulus (MPa) | 2625 | |
Izod Notched Impact Strength (KJ/m2) | 5.4 | ISO 180:2000/Amd.2:2013 |
Charpy Notched Impact قوة(KJ/m2) | 5.9 | ISO 179-1:2010 |
Tensile Modulus (MPa) | 2440 | ISO 527-1:2012 & ISO 527-2:2012 |
Tensile Strength (MPa) | 47.6 | |
Nominal Tensile Strain at Break (%) | 50.6 | |
Thermal Properties | ||
Heat Deflection Temperature (oج) | 52.9 | ISO 75-2:2004 |
طلب
The PLA102 are developed for the application of straws.
Processing Information
PLA102 can be processed on most conventional extrusion molding equipment. The material is stable in the molten state, provided that the drying procedures are followed. Mold flow is highly dependent on melt and mold temperatures. The extrusion temperature is between 180oC and 200oج. علاوة على ذلك, the extrusion molding parameters should be adjusted according to the actual circumstance.
معلومة اضافية
| مكان المنشأ: | شنغهاي, الصين |
|---|---|
| اسم العلامة التجارية: | Hengsi |
| اسم المنتج: | 100% biodegradable and compostable pla granules |
| اللون: | أبيض |
| طلب: | pla straw |
| شهادة: | EN13432.Ok Compost Home |
| اكتب: | 100% Biodegradeble Material PLA |
| اسم آخر: | Polylactic Acid Pellets |
| الكلمات الدالة: | PLA Plastic PLA Granules |
| صفقة: | 25كجم / كيس |