Low density polyethylene resin/LDPE granule/LDPE plastic raw material
وصف
تحديد
1.Virgin or Recycle PE(HDPE,ص,LDPE or LLDPE)
2.Can be used for PE film,shopping bag (blowing),(حقنة) and so on
LDPE plastic granules
Film Grade
العنصر | Test condition | Test Method | Value | Unit |
كثافة |
| ISO 1183 | 0.944-0.955 | ز / سم 3 |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 22 | MPa |
Elongation at break |
| ISO 527-2 | >350 | % |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
VICAT |
| ASTM D-1525 | 126 | درجة مئوية |
Blown Grade
العنصر | Test Condition | Test Method | Value | Unit |
كثافة |
| ISO 1183 | 0.950~0.955 | g/cm |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 24 | MPa |
Elongation at break |
| ISO 527-2 | >600 | % |
Film Grade
العنصر | Test condition | Test Method | Value | Unit |
كثافة |
| ISO 1183 | 0.944-0.955 | ز / سم 3 |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 22 | MPa |
Elongation at break |
| ISO 527-2 | >350 | % |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
VICAT |
| ASTM D-1525 | 126 | درجة مئوية |
Blown Grade
العنصر | Test Condition | Test Method | Value | Unit |
كثافة |
| ISO 1183 | 0.950~0.955 | g/cm |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 24 | MPa |
Elongation at break |
| ISO 527-2 | >600 | % |
معلومة اضافية
| اسم العلامة التجارية: | xy |
|---|---|
| رقم الموديل: | بِكر |
| اللون: | transparent |