100%Biodegradable Polylactic Acid PLA pellets PLA granules PLA plastic raw material
Beschreibung
100%Biodegradable Polylactic Acid PLA pellets PLA granules PLA plastic raw material
Extrusion Molding
PLA 102 is composed of PLA and PBAT, developed for the extrusion molding applications. See Tisch 1 zum properties.
Tisch 1- Typical Material Properties
Physical Properties | Result | Testmethode |
Dichte (g/cm3) | 1.532 | ISO 1183-1:2012 Method EIN |
Melt Mass Flow Rate (g/10min) | 1.62 | ISO 1133-1:2011 Procedure A |
Mechanical Properties |
| |
Flexural Strength (MPa) | 58.9 | ISO 178:2010/Amd. 1:2013 Method A |
Flexural Modulus (MPa) | 2625 | |
Izod Notched Impact Strength (KJ/m2) | 5.4 | ISO 180:2000/Amd.2:2013 |
Charpy Notched Impact Stärke(KJ/m2) | 5.9 | ISO 179-1:2010 |
Tensile Modulus (MPa) | 2440 | ISO 527-1:2012 & ISO 527-2:2012 |
Zugfestigkeit (MPa) | 47.6 | |
Nominal Tensile Strain at Break (%) | 50.6 | |
Thermal Properties | ||
Heat Deflection Temperature (ÖC) | 52.9 | ISO 75-2:2004 |
Anwendung
The PLA102 are developed for the application of straws.
Processing Information
PLA102 can be processed on most conventional extrusion molding equipment. The material is stable in the molten state, provided that the drying procedures are followed. Mold flow is highly dependent on melt and mold temperatures. The extrusion temperature is between 180ÖC and 200ÖC. Moreover, the extrusion molding parameters should be adjusted according to the actual circumstance.
Zusätzliche Information
| Herkunftsort: | Schanghai, China |
|---|---|
| Markenname: | Hengsi |
| Produktname: | 100% biodegradable and compostable pla granules |
| Farbe: | Weiß |
| Anwendung: | pla straw |
| Zertifikat: | EN13432.Ok Compost Home |
| Art: | 100% Biodegradeble Material PLA |
| Anderer Name: | Polylactic Acid Pellets |
| Schlüsselwörter: | PLA Plastic PLA Granules |
| Paket: | 25kg/Sack |