100%Biodegradable Polylactic Acid PLA pellets PLA granules PLA plastic raw material
Περιγραφή
100%Biodegradable Polylactic Acid PLA pellets PLA granules PLA plastic raw material
Extrusion Molding
PLA 102 is composed of PLA and PBAT, developed for the extrusion molding applications. See Table 1 Για properties.
Table 1- Typical Material Properties
Physical Properties | Αποτέλεσμα | Test Method |
Πυκνότητα (g/cm3) | 1.532 | ISO 1183-1:2012 Method ΕΝΑ |
Melt Mass Flow Rate (g/10min) | 1.62 | ISO 1133-1:2011 Procedure A |
Mechanical Properties |
| |
Flexural Strength (MPa) | 58.9 | ISO 178:2010/Amd. 1:2013 Method A |
Flexural Modulus (MPa) | 2625 | |
Izod Notched Impact Strength (KJ/m2) | 5.4 | ISO 180:2000/Amd.2:2013 |
Charpy Notched Impact Δύναμη(KJ/m2) | 5.9 | ISO 179-1:2010 |
Tensile Modulus (MPa) | 2440 | ISO 527-1:2012 & ISO 527-2:2012 |
Αντοχή εφελκυσμού (MPa) | 47.6 | |
Nominal Tensile Strain at Break (%) | 50.6 | |
Thermal Properties | ||
Heat Deflection Temperature (οντο) | 52.9 | ISO 75-2:2004 |
Εφαρμογή
The PLA102 are developed for the application of straws.
Processing Information
PLA102 can be processed on most conventional extrusion molding equipment. The material is stable in the molten state, provided that the drying procedures are followed. Mold flow is highly dependent on melt and mold temperatures. The extrusion temperature is between 180οC and 200οντο. Moreover, the extrusion molding parameters should be adjusted according to the actual circumstance.
Επιπλέον πληροφορίες
| Τόπο καταγωγής: | Σαγκάη, Κίνα |
|---|---|
| Μάρκα: | Hengsi |
| Ονομασία προϊόντος: | 100% biodegradable and compostable pla granules |
| Χρώμα: | άσπρο |
| Εφαρμογή: | pla straw |
| Πιστοποιητικό: | EN13432.Ok Compost Home |
| Τύπος: | 100% Biodegradeble Material PLA |
| Other name: | Polylactic Acid Pellets |
| Λέξεις-κλειδιά: | PLA Plastic PLA Granules |
| Πακέτο: | 25kg/bag |