Low density polyethylene resin/LDPE granule/LDPE plastic raw material
La description
Caractéristiques
1.Virgin or Recycle PE(PEHD,polypropylène,LDPE or LLDPE)
2.Can be used for PE film,shopping bag (blowing),(injection) et ainsi de suite
LDPE plastic granules
Film Grade
Article | Test condition | Test Method | Value | Unité |
Densité |
| ISO 1183 | 0.944-0.955 | g/cm3 |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 22 | MPa |
Elongation at break |
| ISO 527-2 | >350 | % |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
VICAT |
| ASTM D-1525 | 126 | °C |
Blown Grade
Article | Test Condition | Test Method | Value | Unité |
Densité |
| ISO 1183 | 0.950~0.955 | g/cm |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 24 | MPa |
Elongation at break |
| ISO 527-2 | >600 | % |
Film Grade
Article | Test condition | Test Method | Value | Unité |
Densité |
| ISO 1183 | 0.944-0.955 | g/cm3 |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 22 | MPa |
Elongation at break |
| ISO 527-2 | >350 | % |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
VICAT |
| ASTM D-1525 | 126 | °C |
Blown Grade
Article | Test Condition | Test Method | Value | Unité |
Densité |
| ISO 1183 | 0.950~0.955 | g/cm |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 24 | MPa |
Elongation at break |
| ISO 527-2 | >600 | % |
Informations Complémentaires
| Marque: | xy |
|---|---|
| Numéro de modèle: | Vierge |
| Couleur: | transparent |