Low density polyethylene resin/LDPE granule/LDPE plastic raw material
Descrizione
Specifiche
1.Virgin or Recycle PE(HDPE,PP,LDPE or LLDPE)
2.Can be used for PE film,shopping bag (blowing),(injection) e così via
LDPE plastic granules
Film Grade
Elemento | Test condition | Metodo di prova | Value | Unit |
Densità |
| ISO 1183 | 0.944-0.955 | g/cm3 |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 22 | MPa |
Elongation at break |
| ISO 527-2 | >350 | % |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | H |
VICAT |
| ASTM D-1525 | 126 | °C |
Blown Grade
Elemento | Test Condition | Metodo di prova | Value | Unit |
Densità |
| ISO 1183 | 0.950~0.955 | g/cm |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 24 | MPa |
Elongation at break |
| ISO 527-2 | >600 | % |
Film Grade
Elemento | Test condition | Metodo di prova | Value | Unit |
Densità |
| ISO 1183 | 0.944-0.955 | g/cm3 |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 22 | MPa |
Elongation at break |
| ISO 527-2 | >350 | % |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | H |
VICAT |
| ASTM D-1525 | 126 | °C |
Blown Grade
Elemento | Test Condition | Metodo di prova | Value | Unit |
Densità |
| ISO 1183 | 0.950~0.955 | g/cm |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield |
| ISO 527-2 | 24 | MPa |
Elongation at break |
| ISO 527-2 | >600 | % |
Informazioni aggiuntive
| Marchio: | xy |
|---|---|
| Numero di modello: | Vergine |
| Colore: | trasparente |