Boway Alloy Copper Alloy Cickel Silver Nickel Strip C75200
Descrição
Categories: High precision copper alloy strip & plate
Nome: High performance zinc copper alloy nickel strip & plate
Número: C75200
Característica: Elasticity modulus: 115GPa
Good fatigue resistance.
Good electroplate performance
Welding performance is good
Fastness in high temperature
Good cold working, deep drawing, curve performance.
Articles,Chemical composition
| Articles | Chemical composition | |||||
| GB | NÓS | DENTRO | ELE | Cu% | Ni% | Zn% |
| BZn18-26 | C77000 | CuNi18Zn27 | C7701 | 54-58 | 16.5-19.5 | Rem |
Physical properties,fabrication properties
| Physical properties | fabrication properties | |||||||||
| density g/cm3 | electrical conductivity %IACS | thermal conductivity W/(m.K) | modulus of elasticity GPa | specific heat J/(g.K) | cold-workability | machinability | electric plating property | hot dip tin plating property | weldability | corrosion |
| 8.7 | 5 | 32 | 125 | 0.34 | excellent | suitable | excellent | excellent | good | excellent |
Mechanical properties
| Mechanical properties | |||||||||||
| State | Hardness HV | Tension test | dobrar(in rolling direction)rest | dobrar(transverse to rolling direction)test | |||||||
| thickness mm | tensile strength MPa | yield strength MPa | elongation% | thickness mm | angles | ID | espessura | angles | ID | ||
| 1/2H | 150-210 | 0.1-0.7 | 540-655 | ≥390 | ≥8 | ≤1.6 | 180° | 150% of thickness | ≤0.5 | 180° | 300% of thickness |
| ≥0.71 | 540-655 | ≥390 | ≥11 | ||||||||
| H | 180-240 | 0.1-0.7 | 630-735 | ≥390 ≥500 | ≥4 | ≤1.6 | 180° | 200% of thickness | ≤0.5 | 180° | 400% of thickness |
| ≥0.71 | 630-735 | ≥500 | ≥6 | ||||||||
| EH | 210-260 | ≥0.1 | 705-805 | ≥600 | – | ≤1.6 | 90° | 300% of thickness | ≤0.5 | 90° | 600% of thickness |
| SH | 230-270 | ≥0.1 | 765-865 | ≥680 | – | – | – | – | – | – | – |
Typical application
Shields,Liquid crystal oscillators
Articles,Chemical composition
| Articles | Chemical composition | |||||
| GB | NÓS | DENTRO | ELE | Cu% | Ni% | Zn% |
| BZn18-18 | C75200 | CuNi18Zn20 | C7521 | 62-66 | 16.5-19.5 | Rem |
Physical properties,fabrication properties
| Physical properties | fabrication properties | |||||||||
| density g/cm3 | electrical conductivity %IACS | thermal conductivity W/(m.K) | modulus of elasticity GPa | specific heat J/(g.K) | cold-workability | machinability | electric plating property | hot dip tin plating property | weldability | corrosion |
| 8.73 | 6 | 32 | 125 | 0.34 | excellent | suitable | excellent | excellent | good | excellent |
Mechanical properties
| Mechanical properties | |||||||
| State | Hardness HV | Tension test | bending test | ||||
| Thickness mm | Tensile strength MPa | elongation % | espessura | angles | ID | ||
| 0 | – | 0.1-5.0 | ≥375 | ≥20 | ≤1.6 | 180° | sticking closely |
| 1/2H | 120-180 | 0.1-5.0 | 440-570 | ≥5 | ≤1.6 | 180° | 100% of thickness |
| ≤0.5 | 200% of thickness | ||||||
| H | 150-210 | 0.1-0.15 | 540-640 | – | ≤1.6 | 180° | 200% of thickness |
| >0.15-5.0 | ≥3 | ≤0.5 | 400% of thickness | ||||
| EH | ≥185 | 0.1-5.0 | ≥610 | – | – | – | – |
Typical application
Shields,Liquid crystal oscillators,pressing parts
Articles,Chemical composition
| Articles | Chemical composition | |||||
| GB | NÓS | DENTRO | ELE | Cu% | Ni% | Zn% |
| BZn15-20 | C75400 | CuNi15Zn20 | C7541 | 60-64 | 12.5-15.5 | Rem |
Physical properties,fabrication properties
| Physical properties | fabrication properties | |||||||||
| density g/cm3 | electrical conductivity %IACS | thermal conductivity W/(m.K) | modulus of elasticity GPa | specific heat J/(g.K) | cold-workability | machinability | electric plating property | hot dip tin plating property | weldability | corrosion |
| 8.7 | 6 | 32 | 135 | 0.34 | excellent | suitable | excellent | excellent | good | excellent |
Mechanical properties
| Mechanical properties | |||||||
| State | Hardness HV | Tension test | bending test | ||||
| Thickness mm | Tensile strength MPa | elongation % | espessura | angles | ID | ||
| 0 | – | 0.1-5.0 | ≥355 | ≥20 | ≤1.6 | 180° | sticking closely |
| 1/2H | 110-170 | 0.1-5.0 | 410-540 | ≥5 | ≤1.6 | 180° | 100% of thickness |
| H | ≥135 | 0.1-0.15 | ≥490 | – | ≤1.6 | 180° | 200% of thickness |
| >0.15-5.0 | ≥490 | ≥3 | |||||
Typical application
Shields,Liquid crystal oscillators
Informação adicional
| Lugar de origem: | Zhejiang, China |
|---|---|
| Tipo: | Nickel Strip |
| Avaliar: | personalizado |
| Dentro (Mín.): | 45% |
| Resistência (μΩ.m): | personalizado |
| Em pó ou não: | Não em pó |
| Ultimate Strength (≥ MPa): | / |
| Elongation (≥ %): | / |
| Número do modelo: | C75200 |
| Marca: | PW |
| Certificado: | ISO 9001 |
| Nome: | nickel strip |