Competitive Price Magnesia Refractory Bricks Magnesite Bricks for Cement Kilns

Categoria:

Descrição

Competitive Price Magnesia Refractory Bricks Magnesite Bricks for Cement Kilns

Competitive Price Magnesia Refractory Bricks Magnesite Bricks for Cement Kilns

LONGKETER supplying a comprehensive range of FIRED MAG BRICKS.

The fired magnesia brick has high load softening temperature and strong resistance to alkaline slag erosion. The fired magnesia bricks are mainly used for the lining of basic open hearth, wall and bottom of electric furnace, permanent lining of oxygen converter, mixer, non-ferrous smelting furnace, high temperature tunnel kiln, lining of rotary kiln for calcining magnesia and cement, upper lattice bricks of glass melting furnace, bottom and end of steel rolling soaking furnace and heating furnace.

Formulários:

1.Iron Steel Industry

steelmaking furnace lining, ferroalloy furnace, metal mixer furnace lining, converter lining, arc furnace wall and furnace bottom, soaking furnace, heating furnace bottom

2.Non-ferrous metallurgical industry

cobre,nickel,conduzir,zinc,tin smelting furnace lining, refined copper reverberatory furnace,ore electric furnace lining

3.Glass Industry

glass furnace regenerator checker

4.Building Material Industry

lime kiln,cement kiln

5.Refractory Material Industry

High temperature calcination kiln,shaft kiln and tunnel kiln

Descrição do produto

Fired Mag Bricks Product Data

TipoMZ-97AMZ-97BMZ-95AMZ-95BMZ-93MZ-91
MgO (%)≥9796.59594.59391
SiO2 (%)1.0 2.0 2.0 2.0 3.5
CaO (%)2.0 2.0 2.0 3.0
Apparent porosity (%)161816181818
Cold Crushing Strength (MPa)≥60606060
Refractoriness Under Load 0.2MPa°C≥1700165016201560
Reheat test,permanent linear change after heating at (1650°C,2h)%0~ – 0.20~ – 0.30~ – 0.40~ – 0.4
Detail Show

produtos relacionados

Product Categories

Informações da Empresa

Production Show

Fábrica&Oficina

Embalagem & Envio

Informação adicional

Lugar de origem:

Shandong, China

Forma:

Brick

Material:

Magnesium

SiO2 Content (%):

3.5

MgO Content (%):

≥ 93

CaO Content (%):

2

Refractoriness (Degree):

Common (1580°< Refractoriness< 1770°)

Número do modelo:

MZ-93

Marca:

LKT

Apparent porosity (%):

18

Cold Crushing Strength (MPa)≥:

60